烧结工艺对透明氧化铝陶瓷性能的影响

兰州理工大学学报 ›› 2022, Vol. 48 ›› Issue (6): 8-15.

烧结工艺对透明氧化铝陶瓷性能的影响

黄国威^*1, 李婷¹, 孙立¹, 狄正贤², 樊恒中²

1.兰州理工大学省部共建有色金属先进加工与再利用国家重点实验室, 甘肃兰州 730050;
2.中国科学院兰州化学物理研究所固体润滑国家重点实验室, 甘肃兰州 730000

收稿日期:2022-03-26 出版日期:2022-12-28 发布日期:2023-03-21
通讯作者: 黄国威(1987-),男,山东菏泽人,博士,副研究员.Email:huang_guow@163.com
基金资助:
国家自然科学基金(52005235),甘肃省自然科学基金(20JR5RA454),甘肃省科协青年科技人才托举工程项目(GXH20210611-08)

Effect of sintering process on properties of transparent alumina ceramics

HUANG Guo-wei¹, LI Ting¹, SUN Li¹, DI Zheng-xian², FAN Heng-zhong²

1. State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou Univ. of Tech., Lanzhou 730050, China;
2. State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000, China

Received:2022-03-26 Online:2022-12-28 Published:2023-03-21

摘要/Abstract

摘要： 以Isobam600AF为分散剂,Isobam104为胶黏剂,采用注凝成型工艺和真空无压烧结技术,通过改进两步烧结法制备了透明氧化铝陶瓷,探究了不同烧结温度和保温时间对氧化铝陶瓷晶粒尺寸、致密度、光学性能和力学性能的影响.结果表明:该烧结工艺可有效控制晶粒尺寸长大和提高相对密度,进而提高其光学性能和力学性能.在烧结过程中,当温度升高到一定范围时,致密化过程开始,且致密化速率随着温度的升高和保温时间的延长先增加后降低,在两步烧结1 400 ℃保温3 h时致密化速率达到最快.因此,坯体的致密化过程是非线性的,且具有一个最高致密化速率温度和保温时间点.

关键词: 透明氧化铝陶瓷, 烧结工艺, 晶粒尺寸, 光学性能, 力学性能

Abstract: Using Isobam600AF as dispersant and Isobam104 as adhesive, transparent alumina ceramics were prepared by improved two-step sintering method using gelcasting process and vacuum pressureless sintering technology. The effects of different sintering temperatures and holding time on the grain size, density, optical and mechanical properties of alumina ceramics were investigated. The results showed that the sintering process can control the growth of grain sizes and improve the relative density of ceramics effectively, so as to improve their optical properties and mechanical properties. During the sintering process, when the temperature rise to a certain range, the densification process start, and the densification rate first increase and then decreases with the increase of temperature and holding time. The densification rate reaches the fastest value in the condition of the second sintering step holding at 1 400 ℃ for 3 hours. Therefore, the densification of the green body is a nonlinear process with a maximum densification rate temperature and holding time point.

Key words: transparent alumina ceramic, sintering process, grain size, optical properties, mechanical properties

中图分类号:

TB321

黄国威, 李婷, 孙立, 狄正贤, 樊恒中. 烧结工艺对透明氧化铝陶瓷性能的影响[J]. 兰州理工大学学报, 2022, 48(6): 8-15.

HUANG Guo-wei, LI Ting, SUN Li, DI Zheng-xian, FAN Heng-zhong. Effect of sintering process on properties of transparent alumina ceramics[J]. Journal of Lanzhou University of Technology, 2022, 48(6): 8-15.

参考文献

[1] 谢志鹏,刘伟,薄铁柱.透明氧化铝陶瓷制备的研究进展 [J].硅酸盐通报,2011,30(5):1077-1082.
[2] JIANG L,TENG F X,HAO H C,et al.Fabrication and laser parameters of Yb:YAG transparent ceramics with high optical quality [J].Journal of Inorganic Materials,2019,35(2):205-210.
[3] HAN D,ZHANG J,LIU P,et al.Effect of polymorphism of Al₂O₃ on the sintering and microstructure of transparent MgAl₂O₄ceramics [J].Optical Materials,2017,71:62-65.
[4] YUAN X Y,ZHANG F,LIU X J,et al.Fabrication of transparent AlON ceramics by solid-state reaction sintering [J].Journal of Inorganic Materials,2011,26(5):499-502.
[5] 周艳平,王岱峰,奚益明,等.透明氮化铝陶瓷的制备 [J].无机材料学报,1999,14(4):674-678.
[6] 何宇,刘凯歌,肖卓豪,等.透明陶瓷在固态照明中的应用进展 [J].陶瓷学报,2021,42(1):21-35.
[7] WANG S F,ZHANG J,LUO D W,et al.Transparent ceramics:processing,materials and applications [J].Progress in Solid State Chemistry,2013,41(1):20-54.
[8] TRUNEC M,MACA K,CHMELIK R,et al.Polycrystalline alumina ceramics doped with nanoparticles for increased transparency [J].Journal of the European Ceramic Society,2015,35(3):1001-1009.
[9] CHEN H,SHIMAI S,ZHAO J,et al.Highly oriented α-Al₂O₃ transparent ceramics shaped by shear force [J].Journal of the European Ceramic Society,2021,41(6):3838-3843.
[10] 何世权,景然,孟军虎.陶瓷注射成形中Al₂O₃喂料的制备及其脱脂 [J].兰州理工大学学报,2014,40(3):30-34.
[11] YI H,MAO X,ZHOU G,et al.Crystal plane evolution of grain oriented alumina ceramics with high transparency [J].Ceramics International,2012,38(7):5557-5561.
[12] SUN Y,SHIMAI S,PENG X,et al.Gelcasting and vacuum sintering of translucent alumina ceramics with high transparency [J].Journal of Alloys and Compounds,2015,641:75-79.
[13] 张笑,梁森,高忙忙,等.基于注射成型并三步烧结法制备透明氧化铝陶瓷 [J].硅酸盐通报,2016,35(1):250-260.
[14] BERNARD-GRANGER G,GUIZARD C,ADDAD A,et al.Influence of co-doping on the sintering path and on the optical properties of a submicronic alumina material [J].Journal of the American Ceramic Society,2008,91(5):1703-1706.
[15] ASHIKAGA T,KIM B N,KIYONO H,et al.Effect of crystallographic orientation on transparency of alumina prepared using magnetic alignment and SPS [J].Journal of the European Ceramic Society,2018,38(7):2735-2741.
[16] YOSHIMURA H N,GOLDENSTEIN H.Light scattering in polycrystalline alumina with bi-dimensionally large surface grains [J].Journal of the European Ceramic Society,2009,29(2):293-303.
[17] KIM B-N,HIRAGA K,MORITA K,et al.Spark plasma sintering of transparent alumina [J].Scripta Materialia,2007,57(7):607-610.
[18] KRELL A,BLANK P,MA H,et al.Transparent sintered corundum with high hardness and strength [J].Journal of the American Ceramic Society,2003,86(1):12-18.
[19] 刘洪军,刘川,韩龙,等.薄壁陶瓷零件的挤出冷冻3D打印工艺 [J].兰州理工大学学报,2018,44(6):17-23.
[20] SHIMAI S,YANG Y,WANG S,et al.Spontaneous gelcasting of translucent alumina ceramics [J].Opt Mater Express,2013,3(8):1000-1006.
[21] 赵学国,冯涛,王士维,等.透光性氧化铝陶瓷的制备方法[P].中国:CN200510028369.2007-01-31.
[22] CHEN I W,WANG X H.Sintering dense nanocrystalline ceramics without final-stage grain growth [J].Nature,2000,404(6774):168-171.
[23] DONG Y,YANG H,ZHANG L,et al.Ultra-uniform nanocrystalline materials via two-step sintering [J].Advanced Functional Materials,2021,31(1):2007750.
[24] ZHAO J,HARMER M P.Effect of pore distribution on microstructure development:I,matrix pores [J].Journal of the American Ceramic Society,1988,71(2):113-120.
[25] 李继光,孙旭东,王雅蓉,等.α-Al₂O₃纳米粉的烧结动力学 [J].金属学报,1998,34(2):195-199.
[26] FURUKAWA M,IWAHASHI Y,HORITA Z,et al.Structural evolution and the Hall-Petch relationship in an Al-Mg-Li-Zr alloy with ultra-fine grain size [J].Acta Materialia,1997,45(11):4751-4757.
[27] 刘远廷,凌国平,郦剑.纳米Al₂O_3p化学镀铜复合粉末的烧结致密化 [J].中国有色金属学报,2004,14(3):471-478.
[28] FANG Z Z,WANG H.Densification and grain growth during sintering of nanosized particles [J].International Materials Reviews,2008,53(6):326-352.