摘要/Abstract

摘要： 高熵合金因具有高强度、耐腐蚀、耐高温氧化等优异的性能而备受关注.采用铝热反应法制备MoCrFeMnNi高熵合金,用XRD、SEM、EDS、显微硬度和压缩实验研究了铸态及700 ℃/12 h、800 ℃/6 h、1 000 ℃/3 h退火后合金的组织和性能变化.结果表明:铝热法制备的MoCrFeMnNi高熵合金为典型的枝晶形貌,晶体结构主要由BCC相、FCC相以及少量的σ相构成,其中枝晶区域为BCC结构,富含Mo和Cr元素;枝晶间区域为FCC结构,富含Ni元素.随着退火温度的上升,枝晶间逐渐析出纳米级σ相,使得合金硬度上升,在800 ℃/6 h退火处理后达到667 HV,抗压强度达到1 050 MPa;1 000 ℃/3 h退火后,σ相团聚成球状和针状并在高温下部分溶解,σ相的减少使得合金硬度下降,抗压强度与铸态时相当,塑性显著提升.

关键词: 铝热法, 高熵合金, 退火, 组织

Abstract: High entropy alloys have attracted extensive attention due to their high strength, corrosion resistance and high temperature oxidation resistance. In our research, a high-entropy alloy MoCrFeMnNi was prepared by aluminothermic reaction method. Microstructures and properties of 700 ℃/12 h, 800 ℃/6 h, 1 000 ℃/3 h annealed alloys were investigated respectively by XRD, SEM, EDS, microhardness test and compression experiment. The results show that the high entropy alloy MoCrFeMnNi prepared by the aluminothermic method has typical dendritic morphology, and the crystal structure is mainly composed of BCC phase, FCC phase and a small amount of dispersion phase. The dendritic region is BCC structure, rich in Mo and Cr elements. The interdendritic region is FCC structure, rich in Ni element. With the increase of annealing temperature, the nanoscale σ phase is gradually precipitated between dendrites, leading to the increase of alloy hardness, which may reach up to 667 HV and 1 050 MPa after annealing at 800 ℃/6 h. After annealing at 1 000 ℃/3 h, the σ phase agglomerates into a spherical and acicular shape and is partially dissolved at high temperature. With decrease of σ phase, the hardness of the alloy decreases, the compressive strength is equal to that of as-cast state, and the plasticity of the alloy is significantly improved.

Key words: aluminothermic reaction, high entropy alloy, annealing, microstructure

中图分类号:

TG146

喇培清, 王娇, 肖海波, 郑月红, 杨理洁, 盛捷. MoCrFeMnNi高熵合金退火后的组织和性能[J]. 兰州理工大学学报, 2020, 46(5): 1-6.

LA Pei-qing, WANG Jiao, XIAO Hai-bo, ZHENG Yue-hong, YANG Li-jie, SHENG Jie. Microstructure and properties of annealed MoCrFeMnNi high entropy alloys[J]. Journal of Lanzhou University of Technology, 2020, 46(5): 1-6.

参考文献

[1] CANTOR B,CHANG I T H,KNIGHT P,et al.Microstructural development in equiatomic multicomponent alloys[J].Material Science and Engineering A, 2004,375-377:213-218.
[2] YE J W,CHEN S K,LIN S,et al.Nanostructured high-entropy alloys with multiple principal elements:novel alloy design concepts and outcomes[J].Advanced Engineering Materials,2004,6(5):299-303.
[3] ZHANG W,LIAW P K,ZHANG Y.Science and technology in high-entropy alloys[J].China Mater,2018,61(1):2-22.
[4] MIRACLE D B,SENKOV O N.A critical review of high entropy alloys (HEAs) and related concepts[J].Acta Materialia,2017,122:448-511.
[5] LI Z,TASAN C C,PRADEEP K G,et al.A TRIP-assisted dual-phase high-entropy alloy:grain size and phase fraction effects on deformation behavior[J].Acta Mater,2017,131:323-335.
[6] LI D Y,ZHANG Y.The ultrahigh charpy impact toughness of forged Al_xCoCrFeNi high entropy alloys at room and cryogenic temperatures[J].Intermetallics,2016,70:24-28.
[7] LIN Y C,CHO Y H.Elucidating the microstructural and tribological characteristics of NiCrAlCoCu and NiCrAlCoMo multicomponent alloy clad layers synthesized in situ[J].Surface and Coatings Technology,2009,203(12):1694-1701.
[8] HUANG P K,YEH J W,SHUN T T,et al.Multi-principal-element alloys with improved oxidation and wear resistance for thermal spray coating[J].Advanced Engineering Materials,2004,6(1/2):74-78.
[9] CHEN T K,WONG M S,SHUN T T,et al.Nanostructured nitride films of multi-element high-entropy alloys by reactive DC sputtering[J].Surface and Coatings Technology,2004,188-189:193-200.
[10] WANG S P,XU J.TiZrNbTaMo high-entropy alloy designed for orthopedic implants:As-cast microstructure and mechanical properties[J].Materials Science and Engineering C,2017,73:80-89.
[11] CHEN W,TANG Q H,WANG H,et al.Microstructure and mechanical properties of a novel refractory AlNbTiZr high-entropy alloy[J].Materials Science and Technology,2018,34(11):1-7.
[12] HE J Y,LIU W H,WANG H,et al.Effects of Al addition on structural evolution and tensile properties of the FeCoNiCrMn high-entropy alloy system[J].Acta Materialia,2014,62:105-113.
[13] HSU C Y,WANG W R,TANG W Y,et al.Microstructureand mechanical properties of new AlCo_xCrFeMo_0.5Ni high-entropy alloys[J].Advanced Engineering Materials,2010,12(1/2):44-49.
[14] HE F,WANG Z,ZHU M,et al.The phase stability of Ni₂CrFeMo_x multi-principal-component alloys with medium configurational entropy[J].Materials and Design,2015,85:1-6.
[15] 孙娅,吴长军,刘亚,等.合金元素对CoCrFeNi基高熵合金相组成和力学性能影响的研究现状[J].材料导报,2019,33(4):1169-1173.
[16] LA P Q,LU X F,SHEN D,et al.Study on high grade vanadium-aluminium alloy prepared by aluminothermic reaction[J].Powder Metallurgy Technology,2012,30(5):371-375.
[17] STEPANOV N D,YURCHENKO N Y,TIKHONOVSKY M A,et al.Effect of carbon content and annealing on structure and hardness of the CoCrFeNiMn-based high entropy alloys[J].Journal of Alloys and Compounds,2016,687:59-71.
[18] DUPREZ L,DE COOMAN B C,AKDUT N.Deformation behaviour of duplex stainless steel during industrial hot rolling[J].Steel Research,2002,73(12):531-538.
[19] HSU C Y,JUAN C C,WANG W R,et al.On the superior hot hardness and softening resistance of AlCoCr_xFeMo_0.5Ni high-entropy alloys[J].Materials Science and Engineering A,2011,528(10/11):3581-3588.
[20] PRAVEEN S,MURTY B S,KOTTADA R S.Alloying behavior in multi-component AlCoCrCuFe and NiCoCrCuFe high entropy alloys[J].Materials Science and Engineering A,2012,534:83-89.
[21] CHEN Y L,HU Y H,HSIEH C A,et al.Competition between elements during mechanical alloying in an octonary multi-principal-element alloy system[J].Journal of Alloys and Compounds,2009,481(1/2):768-775.
[22] 吴朋慧.AlCoCrCuFeMoNi系多元高熵合金的微结构与性能相关性研究[D].镇江:江苏科技大学,2016.
[23] 赵红艳.高熵固溶体合金的相组成和力学性能研究[D].大连:大连理工大学,2015.
[24] ZHU J M,MENG J L,LIANG J L.Microstructure and mechanical properties of multi-principal component AlCoCrFeNiCu_x alloy[J].Rare Metals,2016,35(5):385-389.