原位观察铜网格增强Al/Cu复合材料的断裂行为

兰州理工大学学报 ›› 2020, Vol. 46 ›› Issue (5): 21-26.

原位观察铜网格增强Al/Cu复合材料的断裂行为

张晓波¹, 张全鑫²

1.兰州理工大学有色金属先进加工与再利用省部共建国家重点实验室, 甘肃兰州 730050;
2.兰州理工大学材料科学与工程学院, 甘肃兰州 730050

收稿日期:2020-02-28 出版日期:2020-10-28 发布日期:2020-11-06
作者简介:张晓波(1981-),男,山西忻州人,博士.
基金资助:
国家自然科学基金(51601084)

In-situ observation of fracture behavior of Cu mesh reinforced Al/Cu composite

ZHANG Xiao-bo¹, ZHANG Quan-xin²

1. State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou Univ. of Tech., Lanzhou 730050, China;
2. College of Materials Science and Engineering, Lanzhou Univ. of Tech., Lanzhou 730050, China

Received:2020-02-28 Online:2020-10-28 Published:2020-11-06

摘要/Abstract

摘要： 将一种按正交法编织的铜网格作为增强体引入到铝基体中制备了Al/Cu复合材料,再借助原位拉伸扫描电镜(SEM),观察了铝铜复合材料的组织演变,研究了其断裂机理与力学性能之间的关系.结果表明:在相同轧制变形量下,25 ℃冷轧和400 ℃热轧均可破碎增强体铜网格,并使其均匀分布于基体铝板.复合板原位拉伸下的载荷-位移曲线均表现出明显的弹性阶段、塑性阶段和失效阶段,微裂纹在Cu颗粒周围和应力集中处萌生,主裂纹及其扩展主要是Cu颗粒周围界面分层开裂与微裂纹沿滑移线方向的扩展共同作用下形成的,并且最终沿滑移线的断裂路径与单轴拉伸方向呈45°.发生在Al层的塑性断裂和Al/Cu结合界面上的界面分层断裂是Al/Cu复合板两种主要的失效方式.

关键词: Al/Cu复合材料, 原位拉伸, 铜网格, 断裂失效

Abstract: A kind of copper mesh woven by orthogonal method was introduced into aluminum matrix as reinforcement phase to prepare Al/Cu composite. The microstructure evolution, the relationship between fracture mechanism and mechanical properties of the Al/Cu composite were both observed and investigated on line by means of in-situ tensile scanning electron microscope (SEM). It is found in this study that under the same rolling deformation, both 25 ℃ cold rolling and 400 ℃ hot rolling may break the reinforced copper mesh and make it uniformly distributed in the matrix aluminum plate. Recorded load-displacement curves of the composite plate under in-situ tension exhibit obvious elastic stage, plastic stage and failure stage. Microcracks initiate around the Cu particles or stress concentrations. The main crack and its propagation are mainly formed by joint action of delamination cracking of the interface around the Cu particles and propagation of the microcracks along the slip line. Finally, the fracture path along the slip line takes 45 °with the uniaxial tensile direction. The plastic fracture of Al layer and the delamination-induced fracture on the Al/Cu bonding interface are the two main failure modes of the Al/Cu composite plate.

Key words: Al/Cu composite, in-situ tension, copper mesh, fracture failure

中图分类号:

TG339

张晓波, 张全鑫. 原位观察铜网格增强Al/Cu复合材料的断裂行为[J]. 兰州理工大学学报, 2020, 46(5): 21-26.

ZHANG Xiao-bo, ZHANG Quan-xin. In-situ observation of fracture behavior of Cu mesh reinforced Al/Cu composite[J]. Journal of Lanzhou University of Technology, 2020, 46(5): 21-26.

参考文献

[1] SAYYAD A S,GHUGAL Y M.Bending,buckling and free vibration of laminated composite and sandwich beams: A critical review of literature[J].Composite Structures,2017,171(7):486-504.
[2] JASWINDER SINGH,AMIT CHAUHAN.Characterization of hybrid aluminum matrix composites for advanced applications-A review[J].Journal of Materials Research and Technology,2016,5(2):159-169.
[3] 张志娟,张兵,尚筱迪,等.Ti/Ni多层复合材料界面扩散行为研究[J].稀有金属材料与工程,2019,48(3):923-930.
[4] 陈剑虹,于洋泊,张晓波.累积叠轧Al/Cu复合板界面反应层核-壳结构形成机制[J].兰州理工大学学报,2020,46(1):1-6.
[5] WANG L,DU Q L,LI C,et al.Preparation of high performance multilayer Cu/Al composite strip by high temperature accumulative rolling[J].Transactions of Nonferrous Metals Society of China,2019,29(8):1621-1630.
[6] LIU C Y,WANG Q,JIA Y Z,et al.Effect of W particles on the properties of accumulatively roll-bonded Al/W composites[J].Materials Science and Engineering,2012,547(6):120-124.
[7] MELAIBARI A,FATHY A,MANSOURI M,et al.Experimental and numerical investigation on strengthening mechanisms of nanostructured Al-SiC composites[J].Journal of Alloys & Compounds,2019,774(6):1123-1132.
[8] 李有堂,李浩勇,宋鸣.铝/钢爆炸焊复合板界面裂纹的扩展路径[J].兰州理工大学学报,2016,42(5):163-166.
[9] 常海,徐超,胡小石.累积叠轧纯Mg/ZK60镁合金层状金属复合材料的组织与性能[J].复合材料学报,2019,36(1):178-185.
[10] XIAO H,QI Z,YU C,et al.Preparation and properties for Ti/Al clad plates generated by differential temperature rolling[J].Journal of Materials Processing Technology,2017,249(11):285-290.
[11] WNAG T,LI S,REN Z,et al.A novel approach for preparing Cu/Al laminated composite based on corrugated roll[J].Materials Letters,2019,234(1):79-82.
[12] LI X,ZU G,WANG P.Effect of strain rate on tensile performance of Al/Cu/Al laminated composites produced by asymmetrical roll bonding[J].Materials Science and Engineering A,2013,575(7):61-64.
[13] 盛捷,喇培清,任军强,等.SEM原位观察双尺度纳米晶304不锈钢的断裂行为[J].兰州理工大学学报,2019,45(2):10-15.
[14] KUMAR A,DUTTA A,MAKENENI S K,et al.In-situ observation of strain partitioning and damage development in continuously cooled carbide-free bainitic steels using micro digital image correlation[J].Materials Science and Engineering,2019,757(5):107-116.
[15] HADDAD M,IVANISENKO Y,COURTOIS-MANARA E,et al.In-situ tensile test of high strength nanocrystalline bainitic steel[J].Materials Science and Engineering,2015,620(1):30-35.
[16] TAYYEBI M,RAHMATABADI D,HASHEMI R,et al.Influence of ARB technique on the microstructural,mechanical and fracture properties of the multilayered Al1050/Al5052 composite reinforced by SiC particles[J].Journal of Materials Research and Technology,2019,8(5):4287-4301.