硝酸改性碳微球的制备及电化学性能

兰州理工大学学报 ›› 2022, Vol. 48 ›› Issue (4): 30-35.

硝酸改性碳微球的制备及电化学性能

寇元哲^*, 刘浩锐, 赵磊

陇东学院机械工程学院, 甘肃庆阳 745000

收稿日期:2011-11-04 出版日期:2022-08-28 发布日期:2022-10-09
通讯作者: 寇元哲(1972-),男,甘肃庆阳人,副教授.Email:625431832@qq.com
基金资助:
甘肃省青年科技基金(20JR10RA137)

Preparation of nitric acid modified carbon microspheres and its electrochemical performance

KOU Yuan-zhe, LIU Hao-rui, ZHAO Lei

School of Mechanical Engineering, Longdong University, Qingyang 745000, China

Received:2011-11-04 Online:2022-08-28 Published:2022-10-09

摘要/Abstract

摘要： 为了提高碳电极材料的比容量,将悬浮聚合法合成的聚苯乙烯微球经高温碳化后,再通过浓HNO₃液相处理制备改性碳微球电极材料.通过场发射扫描电子显微镜、透射电子显微镜、N₂ 吸附解吸仪和傅里叶红外光谱表征所合成碳微球和改性碳微球的形貌和微观结构,以及循环伏安法和恒流充放电法测试改性碳微球电极材料的电化学性能,结果表明:在0.625 A/g的电流密度下改性后碳微球比容量达到246 F/g,且在12.5 A/g的大电流密度下仍然具有比未改性碳微球明显高的比容量.

关键词: 超级电容器, 碳微球, 悬浮聚合, 电化学性能

Abstract: In order to improve the specific capacity of carbon electrode materials, the polystyrene microspheres synthesized by suspension polymerization were carbonized at high temperature, and then modified carbon microspheres electrode materials were prepared by concentrated HNO₃ liquid phase treatment. The morphology and microstructure of the unmodified and modified carbon microspheres were characterized by emission scanning electron microscopy (SEM), transmission electron microscopy (TEM), N₂ adsorption and desorption apparatus and Fourier transform infrared (FTIR) spectrometer,and the electrochemical properties of the modified carbon microspheres electrode materials were measured by cyclic voltammetry (CV) and constant current charge-discharge method. The results showed that the specific capacity of the modified carbon microspheres was up to 246 F/g at the current density of 0.625 A/g, and even at a high current density of 12.5 A/g, the specific capacity of the modified carbon microspheres was still higher than that of the unmodified carbon microspheres.

Key words: supercapacitors, carbon microspheres, suspension polymerization, electrochemical performance

中图分类号:

寇元哲, 刘浩锐, 赵磊. 硝酸改性碳微球的制备及电化学性能[J]. 兰州理工大学学报, 2022, 48(4): 30-35.

KOU Yuan-zhe, LIU Hao-rui, ZHAO Lei. Preparation of nitric acid modified carbon microspheres and its electrochemical performance[J]. Journal of Lanzhou University of Technology, 2022, 48(4): 30-35.

参考文献

[1] LARCHER D,TARASON J M.Towards greener and more sustainable batteries for electrical energy storage [J].Nat Chem,2015,7(1):19-29.
[2] GREY C,TARASCON J.Sustainability and in situ monitoring in battery development [J].Nat Mater,2017,16(1):45-56.
[3] GOODENOUGH J B.Energy storage materials:a perspective [J].Energy Storage Mater,2015,1:158-161.
[4] SUN H,MEI L,LIANG J,et al.Three-dimensional holey-graphene/niobia composite architectures for ultrahigh-rate energy storage [J].Science.2017,356(6338):599-604.
[5] LIN T,CHEN I W,LIU F,et al.Nitrogen-doped mesoporous carbon of extraordinary capacitance for electrochemical energy storage [J].Science.2015,350(6267):1508-1513.
[6] LIANG J,LI F,CHENG H M,et al.On Energy:electrochemical capacitors:capacitance,functionality,and beyond [J].Energy Storage Mater.2017,9:1-3.
[7] LIN Z,GOIKOLEA E,BALDUCCI A,et al.Materials for supercapacitors:when Li-ion battery power is not enough [J].Mater Today,2018,21(4):419-436.
[8] YU M,LIN D,FENG H,et al.Boosting the energy density of carbon-based aqueous supercapacitors by optimizing the surface charge [J].Angew Chem Int Ed,2017,56(20):5454-5459.
[9] YU M,LU Y,ZHENG H,et al.New insights into the operating voltage of aqueous supercapacitors [J].Chemistry-A European Journal,2018,24(15):3639-3649.
[10] TITIRICI M M,WHITE R J,BRUN N,et al.Sustainable carbon materials [J].Chem Soc Rev,2015,44(1):250-290.
[11] BORENSTEIN A,HANNA O,ATTIAS R,et al.Carbon-based composite materials for supercapacitor electrodes:a review [J].J Mater Chem A,2017,5(25):12653-12672.
[12] 李金平,陈晓洁,杨改,等.生物质碳基催化剂对微生物燃料电池的影响 [J].兰州理工大学学报,2019,45(2):73-77.
[13] BARBIERI O,HAHN M,HERZOG A,et al.Capacitance limits of high surface area activated carbons for double layer capacitors [J].Carbon 2005,43(6):1303-1310.
[14] RAYMUNDO-PINERO E,KHOMENKO V,FRACKOWIAK E,et al.Performance of manganese oxide/CNTs composites as electrode materials for electrochemical Capacitors [J].J Electrochem Soc,2005,152(1):229-235.
[15] KIM C.Electrochemical characterization of electrospun activated carbon nanofibres as an electrode in supercapacitors [J].J Power Sources,2005,142(1/2):382-388.
[16] CHANG K W,LIM Z Y,DU F Y,et al.Synthesis of mesoporous carbon by using polymer blend as template for the high power supercapacitor [J].Diam Relat Mater,2009,18(2/3):448-451.
[17] SALINAS-TORRES D,RUIZ-ROSAS R,MORALLON E,et al.Strategies to enhance the performance of electrochemical capacitors based on carbon materials [J].Front Mater,2019,6:115-138.
[18] GUPTA M,SINGH P K,BHATTACHARYA B,et al.Progress,status and prospects of non-porous,heteroatom-doped carbons for supercapacitors and other electrochemical applications [J].Appl Physics A,2019,125(2):122-136.
[19] HU C,DAI L.Carbon-based metal-free catalysts for electrocatalysis beyond the ORR [J].Angew Chem Int Ed,2016,55(39):11736-11758.
[20] BOSTWICK A,SPECK F,SEYLLER T,et al.Observation of plasmarons in quasi-freestanding doped graphene [J].Science,2010,328(5981):999-1002.
[21] ZHANG J,YI X,JU W,et al.Hydrophilic modification of ordered mesoporous carbons for supercapacitor via electrochemically induced surface-initiated atom-transfer radical polymerization [J].Electrochem Commun,2017,74:19-23.
[22] WANG Z,ZHANG W,TAN Y,et al.Electrolyte-philic electrode material with a functional polymer brush [J].ACS Appl Mater Interfaces,2019,11(17):16087-16095.
[23] ZHAO B,HU H,YU A P,et al.Synthesis and characterization of water soluble single-walled carbon nanotube graft copolymers [J].J Am Chem Soc,2005,127(22):8197-8203.
[24] LANG J W,YAN X B,LIU W W,et al.Influence of nitric acid modification of ordered mesoporous carbon materials on their capacitive performances in different aqueous electrolytes [J].J Power Sources,2012,204:220-229.
[25] 冉奋,赵磊,张宣宣,等.纳米棒状锰氧化物的制备及其电化学电容性能 [J].兰州理工大学学报,2013,39(4):23-27.