Ag元素对Ni-7at.%W合金基带织构形成的影响

兰州理工大学学报 ›› 2021, Vol. 47 ›› Issue (1): 5-6.

Ag元素对Ni-7at.%W合金基带织构形成的影响

高忙忙¹, 苏圣尧¹, 张方圆¹, 赵旭¹, 马麟², 索红莉²

1.宁夏大学光伏材料重点实验室, 宁夏银川 750021;
2.北京工业大学材料科学与工程学院, 北京 100124

收稿日期:2020-03-16 出版日期:2021-02-28 发布日期:2021-03-11
作者简介:高忙忙(1982-),男,河北辛集人,副教授.
基金资助:
国家自然科学基金(51501096)

Effect of silver on texture formation of Ni-7at.%W alloy substrates

GAO Mang-mang¹, SU Sheng-yao¹, ZHANG Fang-yuan¹, ZHAO Xu¹, MA Lin², SUO Hong-li²

1. Key Laboratory of Photovoltaic Materials, Ningxia University, Yinchuan 750021, China;
2. College of Materials Science and Technology, Beijing Univ. of Tech., Beijing 100124, China

Received:2020-03-16 Online:2021-02-28 Published:2021-03-11

摘要/Abstract

摘要： Ag元素能够使Ni和Ni-5at.%W合金基带中的晶粒形貌呈细长状,从而提升超导层电流的传输能力.研究了Ag在高W含量的NiW合金基带(>5at.%W)中对织构的影响机制,为后续调控晶粒形貌打下基础.研究表明:Ag使基带中S取向的体积分数降低,进而影响了再结晶后基带中立方晶体型织构的形成.通过在轧制变形量为90%时引入550 ℃保温2 h的中间热处理,可以使冷轧基带的形变因子R由0.72提升至1.05,从而增加铜型织构的体积分数,并使得基带中形变后的立方晶体的取向增大65%.最终,经过再结晶热处理获得了表面立方晶体型织构的体积分数为96.8%的Ni-7at.%W-0.01at.%Ag合金基带.

关键词: 涂层导体, Ni7W合金基带, 织构, Ag元素

Abstract: The Ag element can make grains in the substrates of Ni and Ni-5at.%W alloy elongated so as to improve the current transmission ability of superconducting layer. The mechanism of Ag effect on texture of NiW substrates with high W content (>5at.%W) may be the basis for subsequent control of grain structure morphology. The results show that the presence of Ag decreases volume fraction of S-orientation in substrate, which further affects the formation of cubic crystal texture in the baseband after recrystallization. By introducing intermediate heat treatment at 550 ℃ for 2 h as the rolling deformation reaches about 90%, the deformation factor R of cold rolled baseband can be increased from 0.72 to 1.05, thus increasing the volume fraction of copper texture and increasing the orientation of deformed cubic crystals in the baseband by 65%. Finally, the alloy baseband with a volume fraction of 96.8% Ni-7at.%W-0.01at.%Ag with cubic crystal texture on the surface can be obtained after recrystallization in the heat treatment.

Key words: coated conductors, Ni7W alloy substrate, texture, silver

中图分类号:

TG132.26

高忙忙, 苏圣尧, 张方圆, 赵旭, 马麟, 索红莉. Ag元素对Ni-7at.%W合金基带织构形成的影响[J]. 兰州理工大学学报, 2021, 47(1): 5-6.

GAO Mang-mang, SU Sheng-yao, ZHANG Fang-yuan, ZHAO Xu, MA Lin, SUO Hong-li. Effect of silver on texture formation of Ni-7at.%W alloy substrates[J]. Journal of Lanzhou University of Technology, 2021, 47(1): 5-6.

参考文献

[1] HOLESINGER T G,CIVALE L,MAIOROV B,et al.Progress in nano engineered microstructures for tunable high-current, high-temperature superconducting wires[J].Advanced Materials,2008,20(3):391-407.
[2] YANG F,NARUMI E,PATEL S,et al.In-plane texturing and its effect on critical current densities of YBCO thin films grown on polycrystalline substrates[J]. Physica C:Superconductivity,1995,244(3/4):299-304.
[3] CELENTANO G,VARESI E,PETRISOR T,et al.Influence of the substrate microstructure on the superconducting properties of YBCO coated conductors[J].IEEE Transactions on Applied Superconductivity,2003,13(2):2591-2594.
[4] SARMA V,EICKEMEYER J,SCHULTZ L,et al.Recrystallisation texture and magnetisation behaviour of some FCC Ni-W alloys[J].Scripta Materialia,2004,50(7):953-957.
[5] GOYAL A,PARANTHAMAN M P,SCHOOP U.The RABiTS approach:using rolling-assisted biaxially textured substrates for high-performance YBCO superconductors[J].MRS Bulletin,2004,29(8):552-561.
[6] 高忙忙,索红莉,王丽,等.轧制温度对Ni-9.3%W合金基带形变组织和织构的影响[J].兰州理工大学学报,2016,42(2):13-16.
[7] BULAEVSKII L N,CLEM J R,GLAZMAN L I,et al.Model for the low-temperature transport of Bi-based high-temperature superconducting tapes[J].Physical Review B,1992,45(5):2545-2548.
[8] EICKEMEYER J,SELBMANN D,WENDROCK H,et al.Effect of silver on cube texture formation in nickel substrate tapes[J].Superconductor Science and Technology,2005,18(5):770-775.
[9] GAITZSCH U,RODING C,DAMM C,et al.Elongated grains in Ni5W(Ag) RABiTS tapes[J].Journal of Alloys and Compounds,2015,623:132-135.
[10] EICKEMEYER J,HÜHNE R,GÜTH A,et al.Textured Ni-7.5at.%W substrate tapes for YBCO-coated conductors[J].Superconductor Science and Technology,2008,21(10):105012.
[11] BURGERS W G,MEIJS J C,TIEDEMA T J.Frequency of annealing twins in copper crystals grown by recrystallization[J].Acta Metallurgica,1953,1(1):75-78.
[12] GERVASYEVA I V,RODIONOV D P,SOKOLOV B K,et al.Effect of deformation texture component composition on cube texture formation during primary recrystallization in Ni-based alloys [J].Materials Science ForumEffect of deformation texture component composition on cube texture formation during primary recrystallization in Ni-based alloys [J].Materials Science Forum,2005,495-497(2):1213-1218.
[13] ZHAO Y,SUO H L,ZHU Y H,et al.Study on the formation of cubic texture in Ni-7at.%W alloy substrates by powder metallurgy routes[J].Acta Materialia,2009,57(3):773-781.
[14] BUNGE H J,KÖHLER U.Modelling primary recrystallization in fcc and bcc metals by oriented nucleation and growth with the statistical compromise model[J].Textures and Microstructures,1997,28(3/4):231-259.
[15] 李眉娟,刘丹敏,勾成,等.高温超导Ni-W基带冷轧织构的研究 [R].北京:中国原子能科学研究院年报,2005.
[16] 高忙忙. 涂层导体用织构镍合金基带的研究 [D].北京:北京工业大学,2011.
[17] GERBER P H,TARASIUK J,BACROIX B.Influence of the rolling reduction on static recrystallization in copper [J].Mater Sci Forum,2002,408-412(5):851-856.